1.1 This specification covers carbon and low alloy steel castings having chemical analyses similar to that of the standard wrought grades.
1.2 Several grades are covered and are designated by chemical composition shown in Table 1.
TABLE 1 Chemical Composition (weight, percent)Grade
C
Mn
P, max
S, max
Si
Ni
Cr
Mo
SC 1020
(J02003)
0.18/0.23
0.40/0.80
0.040
0.040
0.30/0.60
. . .
. . .
. . .
SC 1025
(J02508)
0.22/0.28
0.40/0.80
0.040
0.040
0.30/0.60
. . .
. . .
. . .
SC 1030
(J03012)
0.28/0.34
0.50/0.90
0.040
0.040
0.30/0.60
. . .
. . .
. . .
SC 1040
(J04003)
0.37/0.44
0.50/0.90
0.040
0.040
0.30/0.60
. . .
. . .
. . .
SC 1045
(J04502)
0.43/0.50
0.50/0.90
0.040
0.040
0.30/0.60
. . .
. . .
. . .
SC 4130
(J13502)
0.28/0.33
0.40/0.80
0.035
0.040
0.30/0.60
. . .
0.80/1.10
0.15/0.25
SC 4140
(J14045)
0.38/0.43
0.70/1.10
0.035
0.040
0.30/0.60
. . .
0.80/1.10
0.15/0.25
SC 4330
(J23259)
0.28/0.33
0.60/0.90
0.035
0.040
0.30/0.60
1.65/2.00
0.70/0.90
0.20/0.30
SC 4340
(J24053)
0.38/0.43
0.60/0.90
0.035
0.040
0.30/0.60
1.65/2.00
0.70/0.90
0.20/0.30
SC 8620
(J12095)
0.18/0.23
0.60/1.00
0.035
0.040
0.30/0.60
0.40/0.70
0.40/0.60
0.15/0.25
SC 8625
(J12595)
0.23/0.28
0.60/1.00
0.035
0.040
0.30/0.60
0.40/0.70
0.40/0.60
0.15/0.25
SC 8630
(J13095)
0.28/0.33
0.60/1.00
0.035
0.040
0.30/0.60
0.40/0.70
0.40/0.60
0.15/0.25
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3.1 Within the text, the SI units are shown in brackets.
1.3.2 Inch-pound units are applicable for material ordered to Specification A915 and SI units for material ordered to Specification A915M.