ASTM D6383/D6383M-99(2021) PDF

1.1''This practice covers sample preparation temperatures, test parameters, and specimen exposure conditions that are applicable when Test Method D5405/D5405M is used for conducting time-to-failure (creep-rupture) tests of adhesive joints fabricated from ethylene-propylene-diene terpolymer (EPDM) roof membrane material.

1.2''This practice is applicable to joints fabricated in the laboratory from EPDM roof membrane materials and adhesives received from suppliers, and to joints prepared from EPDM seams sampled from field installations.

1.3''The joints are bonded using preformed tape or liquid-based adhesives, and EPDM roof membrane materials that are non-reinforced, fabric- or scrim-reinforced, and fabric backed. Primers are also used as recommended for the specific adhesive.

1.4''This practice contains notes that are explanatory and are not part of the mandatory requirements of this practice.

1.5''The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.

1.6''This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.7''This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.