ASTM B160-05e1 PDF

1.1 This specification covers nickel (UNS N02200)*, low carbon nickel (UNS N02201)*, and solution strengthened nickel (UNS N02211) in the form of hot-worked and cold-worked rod and bar in the conditions shown in Table 1.

1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.

TABLE 1 Mechanical Properties

Condition and Diameter or Distance
Between Parallel Surfaces, in. (mm)Tensile Strength, min,
psi (MPa)Yield Strength (0.2 % offset),
min. psi (MPa)AElongation in 2 in. or 50 mm or 4D, min % Nickel (UNS N02200) Cold-worked (as worked): Rounds, 1 (25.4) and under 80 000 (550) 60 000 (415) 10B Rounds over 1 to 4 (25.4 to 101.6) incl. 75 000 (515) 50 000 (345)15 Squares, hexagons, and rectangles, all sizes 65 000 (450) 40 000 (275) 25B Hot-worked: All sections, all sizes 60 000 (415) 15 000 (105) 35C Rings and disksD - -- Annealed: Rods and bars, all sizes 55 000 (380) 15 000 (105) 40B Rings and disksE - -- Forging quality All sizes F FF Low-Carbon Nickel (UNS N02201) and Solution Strengthened Nickel (UNS N02211) Hot-worked: All sections, all sizes 50 000 (345) 10 000 (70) 40C Annealed: All products, all sizes 50 000 (345) 10 000 (70) 40B

A See 12.2.

B Not applicable to diameters or cross sections under ³/32 in. (2.4 mm).

C For hot-worked flats 5/16 in. (7.9 mm) and under in thickness the elongation shall be 25%, min.

D Hardness B45 to B80, or equivalent.

E Hardness B45 to B70 or equivalent.

F Forging quality is furnished to chemical requirements and surface inspection only. No tensile properties are required.

File Size :	1 file , 96 KB
Note :	This product is unavailable in Russia, Ukraine, Belarus
Number of Pages :	6
Published :	05/01/2005
Redline File Size :	2 files , 180 KB